Transparent Epoxy Resin Potting Glue 2 Parts Silicone Potting Glue Compound 2:1 Low Viscosity For Resistors Sensors Temperature Controllers High Hardness Epoxy Potting Material
Product model
HN-5508 epoxy resin at room temperature or low temperature, with low viscosity, long operation time, good fluidity, and easy penetration into the clearance of the product
Product feature
It has flame retardant insulation, sealing bonding, moisture-proof earthquake resistance, temperature resistance
Product application
HN-5508 is widely used in transformers, resistors, filters, temperature sensors, temperature controllers, ignition coils, high voltage packs
| uring | builder | Epoxy resin 5508 | Curing agent 5508 |
| pigment | Black / White et al | Ruburn / transparent surface |
| | A sticky epoxy resin water | r liquid specific |
| c gravity, g / cm3 | 1.4-1.5 | 1.05 |
| Viscosity of 25℃ | 4,500—6,000cp s | 150—250cp storage |
| e Period (25℃) | Six months | x months |
| processabili | mixing ratio | A: B =5:1 (weight ratio) |
| Available for a time of 25℃ | 2-3H (100g mix) |
| curing time | 25℃ / 6-8H surface stem, 12-16H fully cured or 60-80℃/1.5-2H |
| After curing | 2 Tensile strength of kg/cm | 16-18 |
| 2 Compressive strength of kg/cm | 18-22 |
| Resistance to the voltage of kv/mm | 20-22 |
| Surface resistance ofΩ-cm | 14 1.2*10 |
| Volume resistance ofΩ-cm | 15 1.1*10 |
| contraction percentage% | 0.35-0.55 |
| Water absorption rate was 25℃ * 24H | <0.03% |
| The hardness of SHORE A | 85-95 |
| distortion temperature ℃ | 130-150 |
| low temperature resistant ℃ | -30 |
Matters need attention:
1. This product is an AB agent, according to the label ratio on the product package, and the mixing ratio is weight ratio and non-volume ratio.
2, AB agent mixing can not be stirred with a round bar without resistance, must be stirred with a flat tool with resistance, it is best to use a small mixer.
3. This product should be placed in a cool and dry place to avoid light, keep the workshop dust-free, and cover the unused glue after opening the lid in time.
4. The performance test data is the test result when the humidity is 60% and the temperature is 25℃, for customer reference only.
5, resin glue stored in a wet environment will exhibit a crystallization phenomenon, please put it in the oven at a low temperature hot dry, and restore its original state.