Two Component 10:1 RTV 2 Clear Potting Epoxy Resin Silicone Compound Encapsulant Raw Material For LED Driver

Shenzhen Hanast New Material co.,LTD
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment
Contact Now

Two Component 10:1 RTV 2 Clear Potting Epoxy Resin Silicone Compound Encapsulant Raw Material For LED Driver

Brand Name : Hanast

Model Number : HN-5508AB

Certification : ROHS SGS

Place of Origin : Guangdong, China

MOQ : 1KG

Price : Negotiable

Payment Terms : T/T

Packaging Details : 25KG/barrel

Hardness : Shore D 80

Electrical Insulation : High

Operating Temperature : -40°C to 150°C

Flame Retardant : UL 94 V-0

Thermal Conductivity : 0.8 W/m·K

Dielectric Strength : 500 V/mil

Chemical Resistance : Excellent

Cure Time : 24 hours

Density : 1.71±0.05,g/cm3

Color : Transparent

Shrinkage : Less than 0.1%

Viscosity : 1000 cps

Appearance : Liquid

Mix Ratio : 5:1

Adhesion Strength : 500 psi

Contact Now

Factory Supply Two-Component 10:1 Silicone Encapsulant Waterproof RTV-2 Silicone Potting Rubber Non-corrosive Potting Material For LED Driver

PRODUCT DESCRIPTION

HN-8808, two parts, low viscosity potting compound that cures at room temperature to soft rubber.

* Product Application *

Widely used in sealing, electrical, potting, insulation, antifouling, waterproof, shockproof, coating, electronic appliances, and comprehensive household appliances.

Two Component 10:1 RTV 2 Clear Potting Epoxy Resin Silicone Compound Encapsulant Raw Material For LED Driver

fore curing

builder

Epoxy resin 5508

Curing agent 5508

pigment

Black / White et al

Ruburn / transparent surface

A sticky epoxy resin water

r liquid specific

c gravity, g / cm3

1.4-1.5

1.05

Viscosity of 25℃

4,500—6,000cp s

150—250cp storage

e Period (25℃)

Six months

x months

processabili

mixing ratio

A: B =5:1 (weight ratio)

Available for a time of 25℃

2-3H (100g mix)

curing time

25℃ / 6-8H surface stem, 12-16H fully cured or 60-80℃/1.5-2H

After curing

2 Tensile strength of kg/cm

16-18

2 Compressive strength of kg/cm

18-22

Resistance to the voltage of kv/mm

20-22

Surface resistance ofΩ-cm

14

1.2*10

Volume resistance ofΩ-cm

15

1.1*10

contraction percentage%

0.35-0.55

Water absorption rate was 25℃ * 24H

<0.03%

The hardness of SHORE A

85-95

distortion

temperature ℃

130-150

low temperature resistant ℃

-30

Two Component 10:1 RTV 2 Clear Potting Epoxy Resin Silicone Compound Encapsulant Raw Material For LED DriverTwo Component 10:1 RTV 2 Clear Potting Epoxy Resin Silicone Compound Encapsulant Raw Material For LED Driver

Two Component 10:1 RTV 2 Clear Potting Epoxy Resin Silicone Compound Encapsulant Raw Material For LED Driver

* How to use *

​​ According to the dosage, pour it into the mold after mixing according to A: B=10:1.

Remove the surface bubbles and cure at room temperature (the proportion can be adjusted according to actual needs, the larger the proportion of component B, the faster the curing).

* Packing * ​​

Part A: 10KG / 20KG Plastic Barrel

Part B: 1KG Plastic Barrel


Product Tags:

potting epoxy resin Raw Material

      

RTV 2 potting epoxy resin

      

clear potting compound Raw Material

      
Quality Two Component 10:1 RTV 2 Clear Potting Epoxy Resin Silicone Compound Encapsulant Raw Material For LED Driver for sale

Two Component 10:1 RTV 2 Clear Potting Epoxy Resin Silicone Compound Encapsulant Raw Material For LED Driver Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Shenzhen Hanast New Material co.,LTD
*Subject:
*Message:
Characters Remaining: (0/3000)