3:1 Epoxy Resin Potting Glue for LED Driver Transformers Resistors Power Module High Hardness 2 Parts Transparent Potting Glue Compound
Product Description:
HN-5508 epoxy resin at room temperature or low temperature, with low viscosity, long operation time, good fluidity, and easy penetration into the clearance of the product; no bubbles after curing, smooth surface, luster, high hardness
Main Features:
Flame retardant insulation, sealing bonding, moisture-proof earthquake resistance, temperature resistance
| Before curing | builder | Epoxy resin 5508 | Curing agent 5508 |
| pigment | Black / White et al | Ruburn / transparent surface |
| | A sticky epoxy resin water | r liquid specific |
| c gravity, g / cm3 | 1.4-1.5 | 1.05 |
| Viscosity of 25℃ | 4,500—6,000cp s | 150—250cp storage |
| e Period (25℃) | Six months | x months |
| processabili | mixing ratio | A: B =5:1 (weight ratio) |
| Available for a time of 25℃ | 2-3H (100g mix) |
| curing time | 25℃ / 6-8H surface stem, 12-16H fully cured or 60-80℃/1.5-2H |
| After curing | 2 Tensile strength of kg/cm | 16-18 |
| 2 Compressive strength of kg/cm | 18-22 |
| Resistance to the voltage of kv/mm | 20-22 |
| Surface resistance ofΩ-cm | 14 1.2*10 |
| Volume resistance ofΩ-cm | 15 1.1*10 |
| contraction percentage% | 0.35-0.55 |
| Water absorption rate was 25℃ * 24H | <0.03% |
| The hardness of SHORE A | 85-95 |
| distortion temperature ℃ | 130-150 |
| low temperature resistant ℃ | -30 |
Applications:
storage and transportation
1. Store in a cool and dry place with a storage period of 6 months (25℃).
2. Products beyond the storage period should be confirmed whether there are any abnormalities before being used.
3. Parts A and B of the colloid must be sealed and preserved, with careful leakage during transportation!
4. These kinds of products are non-dangerous goods and can be transported as general chemicals.
Product Tags:
|
|
ODM 3:1 Clear Resin Epoxy Potting Compound Glue For LED Driver 2 Parts Images
|