Tin Cured Liquid Silicone Rubber 100:2 For Cement Cultural Stone Molds High Tear Resistance Liquid Silicone

Condensed Mold Silicone 100:2 Tin Cured Liquid Silicone Rtv 2 Molding Silicone Rubber For Resin Mold Handicraft Indutry Gypsum

Product description:

The main components of condensed silicone rubber mold liquid include: polysiloxane (raw rubber) with hydroxyl end groups and partial side groups, fillers, crosslinking agents, and vulcanization accelerators.
The main components of addition molded silicone rubber include: polysiloxane (raw rubber) with vinyl end groups and some side groups, hydrogen containing silicone oil (crosslinking agent), platinum catalyst (catalyst), and white carbon black (filler).

Application:

The operational time and demolding time after the ratio of silicone and curing agent:
When the amount of curing agent added is 1%, the colloid will still flow after 2.5 hours and can be demolded after 6-8 hours;
When the amount of curing agent added is 2%, the colloid will still flow within 50-1 hour, and demolding can be carried out within 2-3 hours;
When the amount of curing agent added is 3%, the colloid will still flow after 28 to 30 minutes, and demolding can be carried out after 1.5 to 2 hours;
When the amount of curing agent added is 4%, the colloid will still flow within 10-15 minutes and can be demolded within 1-1.5 hours.

Cement Cultural Stone Molds Silicone Rubber

High Tear Resistance Silicone Rubber

Tin Cured Liquid Silicone Rubber

Tin Cured Liquid Silicone Rubber 100:2 For Cement Cultural Stone Molds High Tear Resistance Liquid Silicone Images